| Color: |
WHITE |
Type: |
4 |
|
Application |
|
| Physical Properties: |
Composition Weight % |
| VHN After Firing: |
245 |
Au: |
35 |
| VHN Soft: |
--- |
Pt: |
0 |
| VHN Hard: |
245 |
Pd: |
56.5 |
|
|
Ag: |
0 |
| Proof Stress Soft MPa: |
510 |
Cu: |
0 |
| Proof Stress Hard MPa: |
572 |
Zn: |
X
|
| |
|
Sn: |
3 |
| Tensile Strength Soft MPa: |
715 |
In: |
0 |
| Tensile Strength Hard MPa: |
793 |
Ga: |
4.8 |
| |
|
|
Other Pt Group Metals: |
|
Ru(x) |
|
| Elongation Soft: |
25 |
| Elongation Hard: |
20 |
Au and Pt Group: |
92 |
| Elastic Modulus GPa: |
124 |
Other Metal: |
|
| |
|
PreSolder: |
W, WS, WG |
| Melting Range C: |
1232-1288 |
PostSolder: |
LO, 500 |
| Casting Temp C: |
1371 |
Investment: Phosphate Bonded (Carbon Free) |
| Density g/cc: |
13.9 |
| Expansion at 500C: |
14 |
Crucible: Ceramic |
| Expansion at 600C: |
14.2 |
|
Oxidation Procedure: |
|
650-1040°C,
no hold, Do not remove oxide, no vacuum |
|
| Burnout Temp C: |
815 |