| Color: |
WHITE |
Type: |
4 |
|
Application |
|
| Physical Properties: |
Composition Weight % |
| VHN After Firing: |
245 |
Au: |
0 |
| VHN Soft: |
--- |
Pt: |
0 |
| VHN Hard: |
280 |
Pd: |
79.5 |
|
|
Ag: |
0 |
| Proof Stress Soft MPa: |
608 |
Cu: |
4.9 |
| Proof Stress Hard MPa: |
770 |
Zn: |
2 |
| |
|
Sn: |
4.9 |
| Tensile Strength Soft MPa: |
830 |
In: |
4 |
| Tensile Strength Hard MPa: |
935 |
Ga: |
4.2 |
| |
|
|
Other Pt Group Metals: |
|
Ru(x) |
|
| Elongation Soft: |
28 |
| Elongation Hard: |
14 |
Au and Pt Group: |
80 |
| Elastic Modulus GPa: |
--- |
Other Metal: |
|
| |
|
PreSolder: |
1060W, W, WSF |
| Melting Range C: |
1156-1260 |
PostSolder: |
830W, LO, 500 |
| Casting Temp C: |
1370 |
Investment: Phosphate Bonded (Carbon Free) |
| Density g/cc: |
11.2 |
| Expansion at 500C: |
14.1 |
Crucible: Ceramic |
| Expansion at 600C: |
14.3 |
|
Oxidation Procedure: |
|
650-1010°C,
hold 5 min, remove oxide,no vacuum |
|
| Burnout Temp C: |
820 |